Young’s Modulus of Common Titanium Alloys

The Young’s modulus of titanium alloys typically ranges from 100 to 120 gigapascals (GPa).The following table provides a curated list of Young’s modulus values for common titanium alloys at room temperature (approximately 20°C or 68°F).

Click on the icon to switch between SI (GPa) and US customary/Imperial (ksi) units.

Young’s Modulus Values for Titanium Alloys (Annealed)
UNS numberComposition
Grade 1R50250105
Grade 2R50400105
Grade 3R50550105
Grade 4R50700105
Grade 5R56400Ti-6Al-4V106 - 114
Grade 6R54520Ti-5Al-2.5Sn110 - 125
Grade 7R52400Ti-0.2Pd105
Grade 9R56320Ti-3Al-2.5V91 - 107
Grade 10R58030Ti-11.5Mo-6Zr-4.5Sn108
Grade 11R52250Ti-0.2Pd105
Grade 12R53400Ti-0.3Mo-0.8Ni105
Grade 16R52402Ti-0.06Pd103
Grade 17R52252Ti-0.06Pd103
Grade 18R56322Ti-3Al-2.5V-0.06Pd91 - 107
Grade 19R58153Ti-8V-6Cr-4Mo-4Zr-3Al103
Grade 20R58645Ti-8V-6Cr-4Zr-4Mo-3Al-0.05Pd103
Grade 21R58210Ti-15Mo-3Al-2.7Nb-0.25Si96 - 103
Grade 23R56401Ti-6Al-4V (ELI)106 - 114
Grade 30R53530110
Grade 31R53532110
Grade 36R58450Ti-45Nb62
Timetal® 17R58650Ti-5Al-2Sn-4Mo-2Zr-4Cr109
Timetal® 10-2-3R56410Ti-10V-2Fe-3Al112
Timetal® 1100Ti-6Al-4Zr-2.7Sn-0.4Mo-0.45Si120
Timetal® 15-3R58153Ti-15V-3Al-3Sn-3Cr82 - 111
Timetal® 21SR58210Ti-15Mo-3Nb-3Al-0.2Si83
Timetal® 367R56700Ti-6Al-7Nb105 - 120
Timetal® 550Ti-4Al-4Mo-2Sn-0.5Si110 - 130
Timetal® 551Ti-4Al-4Mo-4Sn-0.5Si113 - 130
Timetal® 6-2-4-2R54620Ti-6Al-2Sn-4Z r-2Mo115
Timetal® 6-2-4-6R56260Ti-6Al-2Sn-4Zr-6Mo115
Timetal® 62STi-6Al-2Fe-0.1Si128
Timetal® 6-6-2R56620Ti-6Al-6V-2Sn115
Timetal® 679Ti-11Sn-5Zr-2.25Al-1Mo-0.2Si105 - 110
Timetal® 685Ti-6Al-5Zr-0.5Mo-0.25Si125
Timetal® 8-1-1R54810Ti-8Al-1Mo-1V124
Timetal® 8-2-9Ti-5.5Al-3.5Sn-3Zr-1Nb-0.25Mo-0.3Si120
Timetal® 834Ti-5.8Al-4Sn-3.5Zr-0.7Nb-0.5Mo-0.35Si-0.06C120
Timetal® 230Ti-2.5Cu105 - 125

The values provided are approximate and can vary depending on various factors such as composition, temperature, and processing methods.

References: 1) Cardarelli, François. Materials Handbook: A Concise Desktop Reference. Switzerland: Springer International Publishing, 2018.