Magnesium ZC-63A-T6 (UNS M16631)
ZC-63A-T6 is a magnesium alloy that is used for casting applications. It is a solution heat treated and artificially aged alloy that has good castability, strength, and machinability.
| Chemical Composition | ||
|---|---|---|
| Element | Min | Max |
| Magnesium | Remainder | |
| Copper | 2.4% | 3.0% |
| Manganese | 0.25% | 0.75% |
| Nickel | 0.01% | |
| Silicon | 0.20% | |
| Zinc | 5.5% | 6.5% |
| Residuals | 0.30% | |
The following table provides a list of magnesium ZC-63A-T6 properties in both SI and US customary/Imperial units.
Click on the icon to switch between Metric and Imperial units.
| Physical Properties | Metric |
|---|---|
| Density | 1870 kg/m3 |
| Mechanical Properties | Metric |
| Tensile Strength (Ultimate) | 248 MPa |
| Tensile Strength (Yield) | 172 MPa |
| Young’s Modulus (E) | 45 GPa |
| Shear Modulus (G) | 17 GPa |
| Elongation at Break in 50 mm | 4% |
| Poisson’s Ratio (ν) | 0.27 |
| Brinell Hardness 500 kg load, 10 mm ball | 55 - 65 |
| Thermal Properties | Metric |
| Melting Point | 465 - 635 °C |
| Solidus | 465 °C |
| Liquidus | 635 °C |
| Thermal Conductivity | 122 W/m·K |
| Specific Heat Capacity (Cp) Typical value for Mg alloys | 0.960 J/g·°C |
| Coefficient of Thermal Expansion (αL) | 27 1/°C |
| Electrical Properties | Metric |
| Electrical Resistivity | 5.40×10-6 Ω·cm |
The values in this table are approximate and can vary depending on various factors such as the specific manufacturing process and heat treatment applied to the alloy.
Advantages & Disadvantages of Magnesium ZC-63A-T6
| Advantages | Disadvantages |
|---|---|
| Strong | Low melting point |
| Lightweight | Corrosion prone |
| Machinable | Poor thermal conductivity |
| Weldable | High cost |
Applications of Magnesium ZC-63A-T6
Magnesium ZC-63A-T6 is a versatile alloy that can be used in a variety of applications, including:
- Automotive industry: Magnesium ZC-63A-T6 is used to make engine blocks, cylinder heads, suspension components, and wheels.
- Aerospace industry: Magnesium ZC-63A-T6 is used to make aircraft parts, missiles, and rockets.
- Marine industry: Magnesium ZC-63A-T6 is used to make boat hulls, propellers, and rudders.
- Industrial sector: Magnesium ZC-63A-T6 is used to make machine tools, robotics, and medical devices.
- Consumer goods sector: Magnesium ZC-63A-T6 is used to make sporting goods, furniture, and jewelry.